Detailed Product Description:

This is a clear conversion coating. As with the more common Alodine® 1201,

Alodine® 1001, is also a registered trademark of Henkel Surface Technologies

and is a chemical treatment process for aluminum used to provide corrosion protection

and as a surface preparation for paint and adhesives. Sometimes called “aluminum

passivation,” it contains hexavalent chromium and is intended to provide corrosion

prevention even when left unpainted.

Alodine® 1001 is used when it is desired to retain the silver-white aluminum appearance

Instead of the more typical gold color of the Alodine 1201 finish.

Chromate conversion is an excellent treatment method to prep aluminum prior to paint

or adhesives since it greatly enhances the ability of an organic coating to form a bond

with the aluminum substrate. Being a surface conversion treatment rather than a coating,

it will not alter the dimensions of the part.

It is frequently used on electrical and electronic equipment because it provides increased

corrosion resistance while remaining electrically conductive.

The Alodine process produces a microscopic thin film commonly prescribed on aluminum

to provide the following surface characteristics:

High-adhesion surface preparation for paint
Improves corrosion resistance
Preserves electrical conductivity of surface
No change in dimensions

Specification & Certifications:

Alodine® 1001 methods and properties are defined by Mil-C-5541-F (Now AMS-C-5541)

and AMS-A-2474. This product is listed on QPL-81706 as certified for Class 3.

Application Notes:

The best results are achieved on wrought alloys (machined billet aluminum alloys).

Good results can also be achieved on type 356 aluminum castings. Type 380 die

casting alloys do not alodine well, however. It should also be noted that the

chemical film is fragile immediately after processing and a 24-hour waiting time

before handling the parts is preferable.

Applications in which temperatures can reach over 120ºF can break down the corrosion resistance

of the coating. In comparison to anodizing, this chemical film is more fragile and

not generally recommended for high-use areas.

This is a clear coating that leaves the surface with the original aluminum appearance.

Surface Preparation:

Aluminum surfaces must be cleaned with a suitable etchant such as Alumiprep 33

or Metal Prep 79, followed by a water rinse.

Immersion Process:

To formulate bath, mix 25 parts Alodine® 1001 concentrate with 75 parts of water. Immersion

time is 2 to 5 minutes. Application temperature can range from ambient up to 100ºF.

Rinse part thoroughly with water and allow to dry. Surface is ready for paint.

Brush-On Process:

Alodine® 1001 solution may be applied by brush or sponge, by using diluted in a 1 to 1 ratio

with water. Assure surface remains fully wet during required contact time of 2 to 5 minutes.

Rinse part with water and surface is ready for paint. 1 quart treats about 100 sq. ft.